en: MRIアーチファクトフリー生体医療用合金の開発

ja: MRIアーチファクトフリー生体医療用合金の開発

en: The Journal of Dental Engineering

ja: The Journal of Dental Engineering


en: MRIでアーチファクトを生じない生体医療用合金の開発

ja: MRIでアーチファクトを生じない生体医療用合金の開発

en: バイオマテリアル-生体材料-

ja: バイオマテリアル-生体材料-


en: Functionalizing of Metal/Intermetallic Laminate Materials by Pulsed Current Hot Pressing (PCHP)

ja: パルス通電圧接法(PCHP)による金属/金属間化合物積層材料の高機能化

en: Ti-aluminides reinforced Ti matrix composites were fabricated from 0.04mm-thcik Ti foils with 0.012mm-thick aluminum foils, using pulsed current hot pressing (PCHP) process, and the effect of processing condition on the properties of composites thus fabricated was investigated. Microstructure of the composite fabricated was an alternatively-laminated structure composed of Ti and Ti-aluminides, and the structure of the Ti-aluminides in the composites changed with increasing a holding temperature during PCHP. Tensile tests carried out for the composites at room temperature revealed that the mechanical properties of the composites changed by altering the holding temperature. The tensile strength and the elongation of the composite produced at 1273 K attained to 810 MPa and 3.64%, respectively. Microstructural observations of fractured specimens showed that the Ti layers effectively bridged numerous cracks emanating from the Ti-aluminides in the composites fabricated at less than 1273 K. In the present review, above results are summarized in comparison with the microstructure and mechanical properties of laminate materials fabricated by conventional vacuum hot pressing.

en: Journal of the Japan Society of Powder and Powder Metallurgy

ja: 粉体および粉末冶金


en: 平成30年度 徳島大学総合教育センターアドミッション部門 報告書

ja: 平成30年度 徳島大学総合教育センターアドミッション部門 報告書

en: 平成30年度 徳島大学総合教育センターアドミッション部門 報告書

ja: 平成30年度 徳島大学総合教育センターアドミッション部門 報告書

misc_type: others


en: 平成29年度 徳島大学総合教育センターアドミッション部門 報告書

ja: 平成29年度 徳島大学総合教育センターアドミッション部門 報告書

en: 平成29年度 徳島大学総合教育センターアドミッション部門 報告書

ja: 平成29年度 徳島大学総合教育センターアドミッション部門 報告書


en: Process and mechanical properties of smart 6061 Al matrix composite by vacuum hot pressing

en: Korean Journal of Materials Research

ja: Korean Journal of Materials Research


en: Ti/TiPd基形状記憶合金ファイバー複合材料の作製とその組織および機械的性質

ja: Ti/TiPd基形状記憶合金ファイバー複合材料の作製とその組織および機械的性質

en: Journal of the Japan Institute Metals

ja: 日本金属学会誌


en: 形状記憶合金繊維強化床用レジンの損傷修復

ja: 形状記憶合金繊維強化床用レジンの損傷修復

en: The Journal of the Japanese Society for Dental Materials and Devices

ja: 歯科材料·器械


en: Material Design of Denture Base Resin Reinforced by Shape Memory Alloy Fiber

ja: 形状記憶合金繊維で強化した床用レジンの材料設計

en: We evaluated the tensile strength of denture base resin reinforced by shape memory alloy fiber. Fiber surface treatment with primer decreased the fiber-pull-out in a shape-memory-fiber reinforced denture base resin matrix composite and increased the tensile strength. We speculated that the increase in tensile strength was caused by an increase in interfacial strength between the fiber and the matrix. Since heat treatment at above 60℃ increased the composite tensile strength, this composite worked as a smartcomposite. Although there was no effect of heat treatment temperature on tensile strength, flexion of composite was observed after heat treatment at a higher temperature, suggesting that the heat treatment temperature should be lower. We speculated that the slight increase in tensile strength after heat treatment was caused by the higher martensite transformation starting temperature of the fiber.

ja: 形状記憶合金繊維で強化した床用レジンの引張強さについて検討した. 繊維表面のプライマー処理により形状記憶合金繊維強化レジン基複合材料の繊維のプルアウトが減少し, 引張強さが増加した. この引張強さの増加は繊維-マトリックス界面強度の増加によると考えられた. 60℃以上での熱処理によって複合材料の引張強さは若干増加したため, この試料がスマート複合材料として機能していることがわかった. 熱処理温度による引張強さの差は認められなかったが, 高温で熱処理した場合, 複合材料の屈曲が認められたため, 熱処理温度は低くすべきだとわかった. 熱処理後の引張強さがあまり増加しなかった理由は, 繊維マルテンサイト変態開始温度が高いためと考えられた.


en: Thermomechanical Behavior of 6061 Al mAtrix Smart Composites Containing 20 vol % TiNi Shape memory Fiber

en: Journal of Materials Processing Technology